OK_EuraCool (ESP-ING)

EuraCool
larson
®
by Alucoil
®
Increasing
Total Solar
Reflectance
larcore
®
by Alucoil
®
PVDF 70% KYNAR 500 RESIN COATING WITH UNIQUE
SOLAR REFLECTIVE PIGMENTS WHICH AFFECT ITS TRS VALUE.
(TOTAL SOLAR REFLECTANCE)
EuraCool byAlucoil increases the total solar reflectance of panels by reducing surface temperature.
An increased product TSR results in higher reflection of solar energy across each area of the solar spectrum.
®
Total Solar Reflectance (TSR) is expressed as the fraction of the incidental solar energy reflected by a panel's surface across the three areas
of the solar spectrum: ultra violet, visible, and infra-red.
BENEFITS & SPECIFICATIONS
► High quality PVDF / Kynar resin coating system
► Reduces panel surface temperatures up to 10 ºC
► Increases paint coating reflectivity
► Darker colors absorb the most solar energy
► Recommended for roofing applications
► Recommended for larger projects >5000m2
► Potential additional 1 LEED point for RSI (Reflective Solar Index > 78%)
► Price adder +6€/m2 for a standard PVdF / Kynar 2 coat paint
PINTURA ESPECIAL PVDF 70% KYNAR 500 CON 30% DE PIGMENTOS ESPECIALES
DE ALTA REFLEXIÓN A LOS RAYOS SOLARES INCIDIENDO EN EL VALOR TRS.
(REFLECTANCIA SOLAR TOTAL)
Las pinturas PVdF EuraCool aumentan la reflectancia solar total reduciendo la temperatura de la superficie de los paneles.
TSR significa que el producto refleja la energía solar en cada zona del espectro solar.
La Reflectancia Solar Total (TSR) se expresa como la fracción de la energía solar que es reflejada por la superficie en las tres zonas del espectro
solar (ultravioleta, visible e infrarrojo).
BENEFICIOS Y ESPECIFICACIONES
► Sistema de lacado de alta calidad (PVdF)
► Reduce la temperatura de la superficie hasta 10 º C
► Aumenta la reflectancia
► Mejores resultados cuanto más oscuro es el color elegido.
► Especialmente recomendado para aplicaciones en cubiertas.
► Disponible para proyectos > 5.000m2.
► Posibilidad de aumentar “LEED CLASS” para RSI (Indice de reflectancia solar > 78%)
► Extracoste aproximado de 6 €/m2 sobre PVdF Bicapa estándar
www.alucoil.com
TECHNICAL DATA SHEET
PROPIEDADS TÉCNICAS
Coating thickness
Espesor de pintura
Primer 7µ (+/- 2µ)
PVdF Top Coat 19-21µ (+/- 2µ)
EN 13523-1
Specular gloss topcoat
Brillo especular
Gloss measured by 60º Gardner: 20-40 g.u.
Brillo medido a 60º Gardner: 20-40 g.u.
EN 13523-2
(Tolerances according to EN 1396, table 4)
Minimum: HB-F
Mínimo HB-F
Pencil hardness
Dureza, método del lápiz
EN 13523-4
Adhesion to cracking on rapid deformation
Resistencia a la deformación rápida
Reverse impact resistance measures by 7,5 Nm/mm No cracks
Resistencia al impacto medida en 7,5 Nm/mm Sin Grietas
EN 13523-5
Adhesion to cracking on rapid deformation after indentation
Adherencia después de corte
Loss of adhesion≤GT1
(More than 95% remains on the surface)
Pérdida de adhesión≤GT1
EN 13523-6
(más del 95% permanece en la superficie)
EN 13523-7
Bending through 180º on flat material up to temper H44
(Minimum T≥1,5 (bending 4 times): No cracks
Doblado a 180º sobre muestra plana, en temple H44
(Mínimo T≥1,5 doblado 4 veces) Sin grietas
Resistance to salt acid spray fog
Resistencia a la niebla salina
After 1000 hours: Corrosion index 3 according EN 1396, table C4
1000 horas de ensayo Clase 3 según la Norma EN 1396, tabla C4
Resistance to cracking on bending
Resistencia al agrietamiento por plegado
EN 13523-8
Resistance to accelerated weathering topcoat
Resistencia a la radiación fluorescente ultravioleta
Resistencia a la condensación de agua
After 500 test hours (=250 hours UV-B)
Slight colour change allowed ang gloss reduction ≤ 10% of the original gloss
EN 13523-10
500 horas de ensayo (250 horas UV-B)
Ligeros cambios de color conforme a Norma Pérdida de brillo <10%
M.E.K / Solvent rubbing test
Resistencia M.E.K
≥80 MEK (Methyl-ethylketon) double rubs
No base material visible
≥80 pasadas dobles
ECCA T11
Heat resistance
Resistencia al envejecimiento acelerado por calentamiento
½ hour by 60ºC continuous metal temperature: No influence
½ horas 60ºC de temperatura del metal continuada Sin influencia
EN 13523-13
After 1000 hours: No influence
Después de 1000 horas Sin influencia
Humidity resistance
Resistencia a la humedad
ASTM D2247-68
TRS DIFERENCE BETWEEN PVDF STANDARD AND PVDF EURACOOL
NORMAL PVdF
EURACOOL PVdF
9% TSR ►
RAL 7015
► 44% TSR
5% TSR ►
RAL 8022
► 38% TSR
12% TSR ►
RAL 7010
► 37% TSR
41% TSR ►
RAL 7035
► 65% TSR
11% TSR ►
RAL 6005
► 32% TSR
13% TSR ►
RAL 5009
► 33% TSR
26% TSR ►
RAL 3011
► 42% TSR
21% TSR ►
RAL 6011
► 35% TSR
18% TSR ►
RAL 7022
► 32% TSR
18% TSR ►
RAL 5008
► 32% TSR
www.alucoil.com
Polígono Industrial de Bayas
C/ Ircio. Parcelas R72-77
09200 Miranda de Ebro, Burgos
SPAIN
Tel.: +34 947 333 320 Fax: +34 947 324 913
[email protected]